Test item 测试名称: Plastic Films and Sheets 塑料薄膜与薄片
Test info 测试内容：
|
Test item |
Test standard |
Lead time |
Sample size |
others |
|
屈服
Package Yield
|
ASTM D4321 |
7 working days |
3m长样品或至少5g样品 |
屈服=单位重量面积 |
|
外观
Appearance
|
GB/T 7707 第5.2节
GB./T 21302 第6.2节
(包装用复合膜、袋)
|
7 working days |
包装应完好无损，膜卷取样时去掉表面三层，再沿膜卷的宽度方向切割取样。 |
在自然光线下目测，并用精度不低于0.5mm的量具测量。 |
|
抗摆锤冲击能量
Pendulum impact resistance
|
NF T54-116 GB/T 21302 第5.4.7节 & 6.5.6节 |
7 working days |
100mm宽，长度尽可能长，保证总长度1m（可累加），需确认测试面 |
|
|
厚度 |
ASTM D 5947 |
7 working days |
A4大小, 1pc |
|
|
ASTM D 374 |
||||
|
ISO 4593 |
||||
|
GB/T 6672 |
||||
|
长度和宽度 |
ISO 4592 |
7 working days |
成品 |
|
|
GB/T 6673 |
||||
|
拉伸强度 |
ASTM D 882 |
7 working days |
A4大小, 5 pcs |
|
|
断裂伸长率 |
||||
|
撕裂强度 |
ASTM D 1004 |
7 working days |
A4大小, 5 pcs |
|
|
ASTM D 1938 |
||||
|
ISO 6383-1 |
||||
|
GB/T 16578.1(裤形撕裂法) |
||||
|
QB/T 1130，JIS K7128-3，DIN 53363， JIS K 6732,AMD.1Section 9.4.1 |
||||
|
摆锤撕裂强度 |
ASTM D 1922 |
7 working days |
A4大小, 5 pcs |
|
|
ISO 6383-2 |
||||
|
GB/T 16578.2 |
||||
|
薄膜落镖冲击强度 |
ASTM D 1709 |
7 working days |
A4大小, 20 pcs |
|
|
ISO 7765-1梯级法) |
||||
|
GB/T 9639.1(梯级法) |
||||
|
热合强度 |
QB/T 2358 |
7 working days |
塑料包装袋，3～5 pcs |
|
|
ASTM F 88-07a |
||||
|
Peel force |
GB/T 8808 |
7 working days |
试样标准尺寸:200mm×15mm, |
|
|
粘连力 Blocking force |
GB/T 16276(塑料薄膜) |
7 working days |
(250~300)×(200~250)mm，送样时样品需两两粘连在一起作为1组试样，至少提供5组试样 |
适用于有至少2层粘连的塑料薄膜 |
|
收缩率 Shrinkage rate |
GB/T 13519第5.6.3节 （聚乙烯热收缩膜） |
7 working days |
建议送样200×150mm, 3pcs |
在试样纵向和横向各画一条对称轴作标记，并标明纵、横向，将试样平放入两框架（带金属网的平行框架）间，接着，迅速浸入120±2℃的恒温介质中自由收缩，20 s后取出，浸入备用的常温浴中，冷却5s后取出试样，水平静置，在30 min内测量纵横对称轴尺寸。精确到1mm，并记录测量数据。 |
|
穿刺强度
Puncture Resistance
|
ISO 13996 |
7 working days |
φ100mm，至少5pcs |
钢针1.0mm，角度30°，100mm/min |
|
GB/T 20655 |
φ100mm，至少5pcs |
钢针1.0mm，角度30°，100mm/min |
||
|
MIL-STD-3010C Test Method 2065 |
250×250mm,10pcs，需确认测试面 |
|
||
|
FED-STD-101C,NOTICE 4 （已废止） |
200×200mm, 5pcs 建议送样250×250mm, 5pcs 需确认测试面 |
|
||
|
薄膜与片材动静态磨擦系数 |
ASTM D 1894 |
7 working days |
A4大小, 1 pc |
|
|
爆破强度 Bursting Strength |
ASTM D751 第18节 |
7 working days |
120*120mm，10pcs |
将样品放入环形夹子中并位于球正下方，以5.00mm/s±0.2mm/s的速度移动夹子或球直到样品破坏。记录此时的力值。 注意圆环内径和压头形状及尺寸 |
|
耐化学试剂抽提性 Resistance to extraction by chemicals |
ASTM D1239 |
7 working days |
50mm×50mm, 3pcs/试剂 |
|
|
无约束包装抗内压破坏 Internal Pressurization Failure Resistance of Unrestrained Packages |
ASTM F1140/F1140M YY/T 0681.3 |
7 working days |
成品包装袋（封口宽度≤30cm），5个 |
|
|
内压法检测粗大泄露（气泡法） Detecting Gross Leaks in Packaging by Internal Pressurization (Bubble Test) |
ASTM F2096 YY/T 0681.5 |
7 working days |
成品包装袋，5个 |
|
|
软包装件密封性（气泡法） Determination of Leaks in Flexible Packaging by Bubble Emission |
GB/T 15171 ASTM D3078 |
7 working days |
软包装件，3件 |
样品所用包装材料不得有各种针孔、裂口及封口处未封和开封等缺陷。 |
|
约束板内部气压法胀破试验 Burst Testing of Flexible Package Seals Using Internal Air Pressurization Within Restraining Plates |
ASTM F2054-F2054M YY/T 0681.9 |
7 working days |
成品包装袋（25.4mm≤宽度和长度≤350mm），5个 |
|
|
镜面光泽度 |
ASTM D 2457 |
7 working days |
最小尺寸: 80mm×20mm, 5 pcs |
|
|
ASTM D 523 |
||||
|
GB/T 8807 |
||||
|
透光率 |
ASTM D 1003-e1 |
7 working days |
50mm×50mm, 3 pcs |
|
|
GB/T 2410- |
||||
|
雾度 |
ASTM D 1003-e1 |
7 working days |
||
|
ISO 14782，JIS K 7361-1 |
||||
|
GB/T 2410，ISO 13468-2 |
||||
|
薄膜脆化温度 |
ASTM D 1790 |
9 working days |
A4大小, 3 pcs |
标准规定在各温度点处理的时间为1h,如果指定处理时间,且该时间超过1h,要参照低温测试报价增加相应费用. |
|
ASTM D 1593clause 10.1.10 |
9 working days |
A4大小, 6 pcs |